Anodising enhances the natural qualities of aluminium
Anodised Cladding & Architectural Fabrications
Anodising is the process by which the natural film on aluminium is greatly increased in thickness.
Aluminium metal is on the anodic side of the galvanic series. Its position is similar to zinc and magnesium, ie it is readily oxidised. The oxide on aluminium is naturally corrosion-resistant, very hard, abrasion-resistant, an insulator and very tenacious. In its natural form, the oxide film on aluminium is less than 0.50 microns thick.
Because the naturally occurring film is very thin and attached to a soft ductile metal, it is easily damaged. Building up this coating provides beneficial properties for the aluminium surface making it perfect for anodised cladding.
Anodising is a process of finishing on aluminium in which the visual appearance of the metal is changed to be aesthetically pleasing. This visual appearance must have colour stability and durability, particularly for exterior use.
The aluminium is anodised by the passing of an electrical current from the anode to the cathode. The item to be anodised becomes the anode part of the electrical circuit whilst the cathodes are already in the anodising tank. The electrical current causes oxygen to be released at the anode which combines with the aluminium to form the aluminium oxide which is the anodic film. The depth of the anodic film is determined by the time in the anodising tank, usually between 15 to 60 minutes which will create an anodic film thickness of between 5 and 25 microns.
The quality of the anodic film is determined by the temperature and concentration of the electrolyte and the current density applied. The anodic film is of a very porous honeycomb structure and must then be sealed in order to achieve the desired weather-resistant properties.
The film produced is porous, hard, transparent and can be coloured in various ways for projects with anodised cladding specified.
Anodising is durable and will not flake, chip, or peel over time.
Anodising is easy to maintain. You only need to do periodic cleaning of anodised extrusions with a mild detergent and water to restore the original lustre.
Ease of fabrication. The marring usually incurred in the fabrication of painted extrusions is virtually non-existent with an anodised extrusion. Other abrasive wear at installation, shipment, and handling is negligible.
Color sustainability, because the sealing process during anodising helps to keep your anodised cladding looking factory new for years to come.